Comportement du béton de sable de dunes renforcé par des fibres métalliques soumis à haute température

Abstract

The aim of this work is to study the mechanical properties of dune sand concretes reinforced with metal fibers and subjected to high temperature. For this, different sand concrete compositions were subjected to a heating-cooling cycle at a rate of 1°C/min. The metal fibers used have lengths of 3 and 5 cm, incorporated with dosages of 0.5; 1 and 1.5%. An improvement of flexural and compressive strength was achieved by metallic fiber concretes subjected to high temperature (150°C, 300°C and 450°C.) at fibers dosage of 1.5%. The best results are obtained by the concretes having a correction of sand with 70% river sand + 30% dune sand.

Ce travail vise a étudié les caractéristiques mécaniques des bétons de sable de dunes renforcés de fibres métalliques et soumis à haute température. Pour cela, différentes compositions de béton de sable ont été soumises à un cycle de chauffage-refroidissement avec une vitesse de 1°C/min. Les fibres métalliques utilisées ont des longueurs de 3 et 5 cm, incorporées avec des dosages de 0,5 ; 1 et 1,5%. Une amélioration de la résistance à la flexion et à la compression a été obtenue par les bétons de fibres métalliques soumis à haute température (150°C, 300°C et 450°C) à dosage de 1,5%. Les meilleurs résultats sont obtenus par les bétons ayant la correction de sable de 70% sable alluvionnaire + 30% sable de dunes.